Carburized and hardened gears have optimum load-carrying capability. There are many alternative ways to produce a hard case on the gear surface. Also, selective direct hardening has some advantages in its ability to be used in the production line, and it is claimed that performance results equivalent to a carburized gear can be obtained. This article examines the alternative ways of carburizing, nitriding, and selective direct hardening, considering equipment, comparative costs, and other factors. The objective must be to obtain the desired quality at the lowest cost.
A widespread weakness of gear drawings is the requirements called out for carburize heat treating operations. The use of heat treating specifications is a recommended solution to this problem. First of all, these specifications guide the designer to a proper callout. Secondly, they insure that certain metallurgical characteristics, and even to some extent processing, will be obtained to provide the required qualities in the hardened gear. A suggested structure of carburizing specifications is give.
Gears are toothed wheels used primarily to transmit motion and power between rotating shafts. Gearing is an assembly of two or more gears. The most durable of all mechanical drives, gearing can transmit high power at efficiencies approaching 0.99 and with long service life. As precision machine elements gears must be designed.
The forming of gear teeth has traditionally been a time-consuming heavy stock removal operation in which close tooth size, shape, runout and spacing accuracy are required. This is true whether the teeth are finished by a second forming operation or a shaving operation.
The most conclusive test of bevel and hypoid gears is their operation under normal running conditions in their final mountings. Testing not only maintains quality and uniformity during manufacture, but also determines if the gears will be satisfactory for their intended applications.
Gear shaving is a free-cutting gear finishing operation which removes small amounts of metal from the working surfaces of the gear teeth. Its purpose is to correct errors in index,
helical angle, tooth profile and eccentricity. The process can also improve tooth surface finish and eliminate, by crowned tooth forms, the danger of tooth end load concentrations
in service. Shaving provides for form modifications that reduce gear noise. These modifications can also increase
the gear's load carrying capacity, its factor of safety and its service life.
The approximate tensile strength of any steel is measured by its hardness, Table 1. Since hardness is determined by both
chemical composition and heat treatment, these are the two important metallurgical considerations in selecting gear steels.